Today's KNOWLEDGE Share:Warpage of a GF filled nylon

-

Today's KNOWLEDGE Share

Warpage of a GF filled nylon part is extremely dependent on temperature and moisture uptake.


Temperature increase is responsible for #matrix expansion (negligible for the fibers though), and moisture uptake produces matrix swell (again GF does not care much).So if a part is warped when dry as molded at room temperature (that is what simulation codes will predict for you !!) it will tend to "UNWARP" as you heat the part or let it uptake moisture.


This effect can perfectly be simulated, if you account properly for the anisotropic elastic properties and #fiberorientation and know the swell rate with water uptake.


For #temperature induced UNWARP you will need detailed CTE (T) in x, y and z though to get it right ! Those CTE's, with the needed level of detail, are not available directly from Flow Analysis codes for the moment, but e-Xstream engineering, part of Hexagon’s Manufacturing Intelligence division Digimat software can provide those.


Source:Vito Leo

Follow: http://polymerguru.blogspot.com


#polymers #plasticindustry #nylon #glassfiber #temperature #moisture

Comments

Post a Comment

Popular posts from this blog

Today's KNOWLEDGE Share:PLA BOTTLE

-
Image
Today's KNOWLEDGE Share Ever wondered how we can reduce plastic pollution in India? The Mysuru-based Defence Food Research Laboratory (DFRL), affiliated with the DRDO, has launched an eco-friendly remedy with the introduction of biodegradable water bottles. Crafted from sustainable Polylactic acid (PLA) material, these bottles not only combat plastic waste but also contribute to reducing the overall carbon footprint. The best thing about this bottle is its all-encompassing sustainability approach – the bottle, cap, and label are all compostable. This innovation, derived from 100% bio-based and renewable sources, sets us on a path towards environmental conservation and fosters a greener and more sustainable future. Source:The Better India #polymers #bioplastics #pla   #compostable   #ecofriendly   #sustainability
Read more

Opportunities in United States

-
Dear Members,  If you are looking for a new position in the United States,here are my personal recommendations to those who reside in the USA.  This portal is offering many roles from Junior to senior levels.You can stumble upon it to find a relevant position that suits your profile.  Pls visit the link:https://urbanlocalcmp.page.link/kEnz1gQdAmyySqrY8
Read more

Today's KNOWLEDGE Share:High and low shear rate changes in Rheology

-
Image
Today's KNOWLEDGE Share If a relatively high Mw grade flows from thin to thick, as shown in the picture, and if the time needed to fill the thick section is way shorter than the average polymer relaxation time, the polymer will not be able to reach its higher viscosity (corresponding to higher thickness/lower shear-rate). I am assuming here the polymer reached equilibrium low viscosity in the thin section, say for instance because it is much longer. Any pressure prediction not accounting for transient rheology would then overpredict the pressure to fill.Of course the diverging flow will further complicate the situation and mess with the molecular orientation created in the thin section, but to what extent ? Since this is more of a reasonable "conjecture", don't take this for granted, and discuss or share your opinion in the comments. There are hundreds of Rheology papers on the "4:1 contraction flow". Not sure I have ever seen any on the..."1:4 expansio
Read more