Today's KNOWLEDGE Share:Biobased Plastic materials challenges

-

Today's KNOWLEDGE Share

When trying to move to plant-based or biosourced plastic materials, a whole host of challenges will come-up.


Due to intrinsically lower Tg of bio-materials, chances are that you will have to transition to semi-crystalline materials and develop a very skillful mastering of precise shrinkage control in your molding process. Subtle physical phenomena including molecular orientation, flow induced crystallinity, slow dimensional recovery by relaxation will make your life a bit more complicated.


Lower thermal stability will also seriously tighten-up your limits in terms of thermal control and residence time in your process. Drying may suddenly become a critical step too.

Overall, a much better and deeper understanding of the molding process and specific plastic materials will be needed to address these challenges.


Source:Vito Leo

Follow: http://polymerguru.blogspot.com


#plastics #biobased #injectionmolding #shrinkage #semicrystalline #thermal #orientation


Comments

Post a Comment

Popular posts from this blog

Today's KNOWLEDGE Share:PLA BOTTLE

-
Image
Today's KNOWLEDGE Share Ever wondered how we can reduce plastic pollution in India? The Mysuru-based Defence Food Research Laboratory (DFRL), affiliated with the DRDO, has launched an eco-friendly remedy with the introduction of biodegradable water bottles. Crafted from sustainable Polylactic acid (PLA) material, these bottles not only combat plastic waste but also contribute to reducing the overall carbon footprint. The best thing about this bottle is its all-encompassing sustainability approach – the bottle, cap, and label are all compostable. This innovation, derived from 100% bio-based and renewable sources, sets us on a path towards environmental conservation and fosters a greener and more sustainable future. Source:The Better India #polymers #bioplastics #pla   #compostable   #ecofriendly   #sustainability
Read more

Opportunities in United States

-
Dear Members,  If you are looking for a new position in the United States,here are my personal recommendations to those who reside in the USA.  This portal is offering many roles from Junior to senior levels.You can stumble upon it to find a relevant position that suits your profile.  Pls visit the link:https://urbanlocalcmp.page.link/kEnz1gQdAmyySqrY8
Read more

Today's KNOWLEDGE Share:High and low shear rate changes in Rheology

-
Image
Today's KNOWLEDGE Share If a relatively high Mw grade flows from thin to thick, as shown in the picture, and if the time needed to fill the thick section is way shorter than the average polymer relaxation time, the polymer will not be able to reach its higher viscosity (corresponding to higher thickness/lower shear-rate). I am assuming here the polymer reached equilibrium low viscosity in the thin section, say for instance because it is much longer. Any pressure prediction not accounting for transient rheology would then overpredict the pressure to fill.Of course the diverging flow will further complicate the situation and mess with the molecular orientation created in the thin section, but to what extent ? Since this is more of a reasonable "conjecture", don't take this for granted, and discuss or share your opinion in the comments. There are hundreds of Rheology papers on the "4:1 contraction flow". Not sure I have ever seen any on the..."1:4 expansio
Read more